http://dspace.udla.edu.ec/handle/33000/9168| Tipo de material : | bachelorThesis |
| Título : | Diseño y construcción de una columna con piedra caliza para reducción de hierro y cobre en agua de drenaje ácido de mina |
| Autor : | Loayza Jaramillo, Luis Felipe |
| Tutor : | Black Solís, Indira Fernandina |
| Palabras clave : | IMPACTO AMBIENTAL;DRENAJES ÁCIDOS DE MINAS;AGUAS RESIDUALES |
| Fecha de publicación : | 2018 |
| Editorial : | Quito: Universidad de las Américas, 2018 |
| Citación : | Loayza Jaramillo, L. F. (2018). Diseño y construcción de una columna con piedra caliza para reducción de hierro y cobre en agua de drenaje ácido de mina (Tesis de pregrado). Universidad de las Américas, Quito. |
| Resumen : | La siguiente investigación se llevó a cabo en el laboratorio L12 de la Universidad de las Américas, sede Queri, donde, se construyó una columna de tratamiento en acrílico, tomando datos bibliográficos y criterios de diseño, para luego, realizar ensayos experimentales, con 3 repeticiones, las cuales, consistieron en colocar diferentes granulometrías de piedra caliza (5-10, 15-20, 25-30) mm, para conocer el tiempo de residencia del sistema con ayuda de un trazador... |
| Descripción : | The following research was carried out in the L12 laboratory of the UDLA, Queri, where a column of acrylic treatment was constructed, taking bibliographic data and design criteria, to then carry out experimental tests, with 3 repetitions, which consisted of placing different granulometries of limestone (5-10, 15-20, 25-30) mm, to know the residence time of the system with the help of a tracer. The best treatment was chosen using an ANOVA. Then, 120 liters of acid drainage water (AMD) was collected at the exit of a mining project in the Portovelo Canton, Provincia del Oro, to carry out the project on an experimental scale. The AMD underwent a treatment that was based on using a 15 gallon tank connected to an upflow column through a submersible pump, which contained limestone with a particle size of 5mm to 10mm obtained from the experimental design. PH, Fe, and Cu measurements were taken at the beginning and at the end of the treatment in a certified laboratory. The initial pH value of AMD was 1.99 and the treated was 7.24; and the percentage of removal was: Fe (99.9 per cent) and Cu (99.1 per cent). This treatment system has a high removal of metals put to study and in accordance with the results obtained from the laboratory, the discharge complies with the national environmental regulations. |
| URI : | http://dspace.udla.edu.ec/handle/33000/9168 |
| Aparece en las colecciones: | Ingeniería Ambiental en Prevención y Remediación |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| UDLA-EC-TIAM-2018-15.pdf | 2,52 MB | Adobe PDF | Visualizar/Abrir |
Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons